bercoweld S2

With the electrode bercoweld S2, welding and brazing processes of automotive engineering can be significantly improved. This copper electrode for welding and brazing provides optimized flowing properties, better ability to bridge root openings and higher processing speed.

Range of application

bercoweld S2

This welding filler metal is particularly recommended for the use of coated sheets for the car industry. Good flowing properties of weld pool, no tendency to porosity and spatter. Suitable for welding of Cu and Cu-alloys as well as low and unalloyed steels and cast iron.

MIG – pulsed-arc welding is recommended.
WIG – for sheets thicker than 3,00 mm preheating to apprx. 250-300 °C is recommended.

Standard designation and composition

ISO 24373CuSi2Mn1 Cu6511
Cubalance
Si1,70-1,90
P0,008-0,012
Mn0,90-1,10
Sn0,17-0,25

Physical standard data

Densitykg/dm³8,7
Melting range°C1030-1050
Thermal conductivityW / m x K40
Coefficient of linear mean expansion10-6/K18,1
Electric conductivitym / Ω x mm²4,7-5,3
ResistivityΩ x mm² /m0,188-0,213

Mechanical properties of the weld joint, standard data

Heat treatment non treated
Tensile strengthN/mm²285
Elongation%45
Brinell hardnessHB 2,5/62,562
Notched bar impact testAv (J)75

Delivery programme

Make-upWeight/LengthDimension
Drum / bedrabox175 - 200 kg0,80 - 1,60 mm
SD300 / BS300 / K30012 - 15 kg0,80 - 2,40 mm
H500 / H560 / H760150 - 250 kg0,80 - 2,40 mm
Coils25 - 100 kg1,60 - 6,00 mm
Rods250 - 3000 mm1,60 - 6,00 mm

Recommended inert gas

Argon4.8/ 5.0/ 5.3/ 5.6/ 6.0

Further product information

bercoweld S2

In this brochure you will find all details about the brazing electrode bercoweld S2.

PDF download

bercoweld S2

Data sheet for bercoweld S2.

PDF download